Indian Government’s Department of Science & Technology announced that scientists have developed low-cost Fe-based intermetallic powders that can be used as a corrosion-resistant coating for materials exposed to harsher environments like high temperature in thermal power plants where oxidation, corrosion, and wear and tear takes place simultaneously. The coatings showed 4 times increased corrosion resistance in the aqueous corrosive media than the mild steel.Wear and corrosion cause major damage over a range of service temperatures. Hence, there is a need to protect the component surface with a suitable material for enhanced economic viability. Such surface coating on a turbine blade can enhance the service life and hence increases the operation hours of turbine. At present, thermally sprayed Chromium Carbide-Nickel Chromium Powder and Tungsten Carbide-Cobalt (Cr3C2-NiCr and WC-Co) (cermet) coatings have been widely used for superior wear and high-temperature oxidation resistance applications like thermal power plant turbine blades, aerospace engine blades, landing gear shafts, steel rolls in the paper industry. This is mainly attributed to their hardness, toughness, and better corrosion resistance under exposure to up to 550 degree Celsius in the case of WC-Co coatings and up to 850 degree Celsius for CrC-NiCr coatings. However, the powders are expensive due to presence of Co and Ni elements. Besides, Cr is toxic in its hexavalent state. Replacement of these coatings with simple Fe-based coatings with novel microstructural constituents is very promising. In this regard, iron-based solid phases involving two or more metallic or semi metallic elements (intermetallics) can play a major role owing to their hardness and better corrosion resistance. However, their deployment is rather restricted by low ductility.A team of scientists of Department of Science & Technology R&D Centre for Engineered Coatings of International Advanced Research Centre for Powder Metallurgy & New Materials has addressed this by synthesizing Fe-based intermetallic powders and utilized the same for depositing the coatings using detonation spray coating technique. Besides, ARCI has developed gas atomized Fe aluminide powder and deposited it on mild steel substrates by DSC without any cracks or spalling. The coatings have demonstrated 4 times increased corrosion resistance in the aqueous corrosive media than the mild steel.The coatings exhibited better corrosion resistance when Cr and Al are in a solid solution with Fe than in the Fe –rich phases. The coatings have demonstrated an increased wear resistance by 30-40% than the mild steel under solid particle erosion wear mode, implying that FeAlCr coatings can be used for high-temperature erosion resistance applications. More studies are currently underway to qualify the FeAlCr coatings for fireside corrosion protection of boiler components in collaboration with the NTPC, to enhance boiler life.
Indian Government’s Department of Science & Technology announced that scientists have developed low-cost Fe-based intermetallic powders that can be used as a corrosion-resistant coating for materials exposed to harsher environments like high temperature in thermal power plants where oxidation, corrosion, and wear and tear takes place simultaneously. The coatings showed 4 times increased corrosion resistance in the aqueous corrosive media than the mild steel.Wear and corrosion cause major damage over a range of service temperatures. Hence, there is a need to protect the component surface with a suitable material for enhanced economic viability. Such surface coating on a turbine blade can enhance the service life and hence increases the operation hours of turbine. At present, thermally sprayed Chromium Carbide-Nickel Chromium Powder and Tungsten Carbide-Cobalt (Cr3C2-NiCr and WC-Co) (cermet) coatings have been widely used for superior wear and high-temperature oxidation resistance applications like thermal power plant turbine blades, aerospace engine blades, landing gear shafts, steel rolls in the paper industry. This is mainly attributed to their hardness, toughness, and better corrosion resistance under exposure to up to 550 degree Celsius in the case of WC-Co coatings and up to 850 degree Celsius for CrC-NiCr coatings. However, the powders are expensive due to presence of Co and Ni elements. Besides, Cr is toxic in its hexavalent state. Replacement of these coatings with simple Fe-based coatings with novel microstructural constituents is very promising. In this regard, iron-based solid phases involving two or more metallic or semi metallic elements (intermetallics) can play a major role owing to their hardness and better corrosion resistance. However, their deployment is rather restricted by low ductility.A team of scientists of Department of Science & Technology R&D Centre for Engineered Coatings of International Advanced Research Centre for Powder Metallurgy & New Materials has addressed this by synthesizing Fe-based intermetallic powders and utilized the same for depositing the coatings using detonation spray coating technique. Besides, ARCI has developed gas atomized Fe aluminide powder and deposited it on mild steel substrates by DSC without any cracks or spalling. The coatings have demonstrated 4 times increased corrosion resistance in the aqueous corrosive media than the mild steel.The coatings exhibited better corrosion resistance when Cr and Al are in a solid solution with Fe than in the Fe –rich phases. The coatings have demonstrated an increased wear resistance by 30-40% than the mild steel under solid particle erosion wear mode, implying that FeAlCr coatings can be used for high-temperature erosion resistance applications. More studies are currently underway to qualify the FeAlCr coatings for fireside corrosion protection of boiler components in collaboration with the NTPC, to enhance boiler life.
